Description
Born2Bon Ultra HV adhesives are low-odor, low-blooming, instant adhesives with a range of viscosities, specially designed for bonding most substrates including plastics and rubbers. The formulation consistency has been designed for high bond strength, even in places that are subject to flexing. Careful selection of the formulation ingredients ensures that the product does not stain areas close to the adhesive joint.
KEY FEATURES
→ Fixture time : 10 seconds (depending on substrates)
→ High bonding strength
→ Long open time
→ Low blooming
→ Less brittle than conventional instant adhesives
→ Bonds a large range of materials**, including polystyrene
→ Transparent and easy to use
→ Low-Odor
APPLICATIONS
Typical applications for this product are leather and rubber bonding, shoe assembly, automotive aftermarket applications, speaker assembly, and car wheel bonding
PRODUCT CHARACTERISTICS
Base Technology: Methoxyethyl Cyanoacrylate
Components 1k – 2k: 1k
Appearance/Color: Transparent
Temperature Use Range: -40°C to 80°C (-40°F to 176°F)
VOC Content (ISO 11890-2): 42 g/L
UNCURED PHYSICAL PROPERTIES
Viscosity at 25°C (77°F)*: 700 – 1,000 cP
Specific Gravity (ASTM D1875: 23°C / 73.4°F): 1.12 g/mL
Refractive Index, ABBE: 1.47 – 1.48
*based on Brookfield viscometer
CURED PHYSICAL PROPERTIES
Soft Point – HDT (ASTM E2092-18a): 56°C (132.8°F)
Glass Transition Temperature (ISO 6721): 79°C (174.2°F)
Coefficient of Linear Thermal Expansion (ISO 10545-8): 30 x 10-6
Water Absorption (after 24 hrs) (ASTM D542): 2.3%
Impact Resistance (after 24 hrs)(ISO 9653): 9.0 kJ/m2
Electrical Properties of Resistivity IEC 60093
Surface resistivity DC 500 V (Ohm): 2.9·1014
Volume resistivity DC 1kV (Ohm.m): 7.5·1013
Corrected Dissipation Factor, Dielectric Constant IEC 60250
D @ 1 kHz: 0.0222
k’ @ 1 kHz: 3.22
D @ 1 MHz: 0.0168
k’ @ 1 MHz: 3.04
BONDING PERFORMANCE
Lap shear strength (ISO 4587) @ 23°C (73.4°F) (MPa)
@ 2mm/min after 24h Curing at RT
Grit-Blasted Mild Steel (GBMS): 11 (+/- 1)
Aluminum (A5754): 4 (+/- 1)
ABS: 6 (+/- 1) SF
PVC: 8 (+/- 1) SF
Phenolic: 5 (+/- 2)
Polycarbonate: 4 (+/- 1) SF
@ 100mm/min after 24h Curing at RT
Nitrile: 0.5 (+/- 0.1) SF
Neoprene: 0.3 (+/- 0.1) SF
@ 2mm/min after 1 Week Curing at RT
Grit-Blasted Mild Steel (GBMS): 15 (+/- 1)
T-Peel Strength @ 23°C (73.4°F) (N/mm)
@100mm/min after 1 week curing @ RT
EPDM: 2.0 (+/- 0.4) SF